1LB NYLON RESIN DUPONT Zytel® 70G33L NC010 Injection Molding.

Description

Zytel® 70G33L NC010 is a 33% glass fiber reinforced polyamide 66 resin for injection molding.
Processing/Physical Characteristics
dry / cond
Unit
Test Standard
ISO Data
Molding shrinkage, parallel
0.3 / *
%
ISO 294-4, 2577
Molding shrinkage, normal
1.1 / *
%
ISO 294-4, 2577
Thermal conductivity of melt
0.22
W/(m K)
-
Spec. heat capacity of melt
2210
J/(kg K)
-
Ejection temperature
210
°C
-
ASTM Data
Mold Shrinkage, MD
0.002
mm/mm
ASTM D 955
Mold Shrinkage, TD
0.01
mm/mm
ASTM D 955
Mechanical properties
dry / cond
Unit
Test Standard
ISO Data
Tensile Modulus
10000 / 8000
MPa
ISO 527
Stress at break
200 / 140
MPa
ISO 527
Strain at break
3.5 / 5
%
ISO 527
Tensile creep modulus, 1h
* / 8000
MPa
ISO 899-1
Tensile creep modulus, 1000h
* / 5500
MPa
ISO 899-1
Charpy impact strength, +23°C
85 / 100
kJ/m²
ISO 179/1eU
Charpy impact strength, -30°C
70 / 75
kJ/m²
ISO 179/1eU
Charpy notched impact strength, +23°C
13 / 17
kJ/m²
ISO 179/1eA
Charpy notched impact strength, -30°C
10 / 10
kJ/m²
ISO 179/1eA
Abrasion resistance
10 / *
mm³
ISO 4649
ASTM Data
Tensile Strength
186 / -
MPa
ASTM D 638
Elongation at Break
3 / -
%
ASTM D 638
Flexural Modulus
8965 / -
MPa
ASTM D 790
Flexural Strength
262 / -
MPa
ASTM D 790
Izod Impact notched, 1/8 in
117 / -
J/m
ASTM D 256
Thermal properties
dry / cond
Unit
Test Standard
ISO Data
Melting temperature, 10°C/min
262 / *
°C
ISO 11357-1/-3
Glass transition temperature, 10°C/min
80 / *
°C
ISO 11357-1/-2
Temp. of deflection under load, 1.80 MPa
252 / *
°C
ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa
261 / *
°C
ISO 75-1/-2
Coeff. of linear therm. expansion, parallel
18 / *
E-6/K
ISO 11359-1/-2
Coeff. of linear therm. expansion, normal
83 / *
E-6/K
ISO 11359-1/-2
Burning Behav. at 1.5 mm nom. thickn.
HB / *
class
IEC 60695-11-10
Thickness tested
1.5 / *
mm
-
Yellow Card available
yes / *
-
-
Burning Behav. at thickness h
HB / *
class
IEC 60695-11-10
Thickness tested
0.7 / *
mm
-
Yellow Card available
yes / *
-
-
Burning rate, FMVSS, Thickness 1 mm
28
mm/min
ISO 3795 (FMVSS 302)
Oxygen index
24 / *
%
ISO 4589-1/-2
ASTM Data
UL 94 Flame rating
HB
-
UL 94
Thickness tested
1.5
mm
-
Coefficient of Thermal Expansion, MD
18
E-6/K
ASTM D 696
Coefficient of Thermal Expansion, TD
83
E-6/K
ASTM D 696
DTUL @ 66 psi
261
°C
ASTM D 648
DTUL @ 264 psi
249
°C
ASTM D 648
Melting Temperature
263
°C
ASTM D 3418
Electrical properties
dry / cond
Unit
Test Standard
ISO Data
Relative permittivity, 100Hz
4.2 / -
-
IEC 62631-2-1
Relative permittivity, 1MHz
4 / -
-
IEC 62631-2-1
Dissipation factor, 100Hz
100 / -
E-4
IEC 62631-2-1
Dissipation factor, 1MHz
150 / -
E-4
IEC 62631-2-1
Volume resistivity
1E13 / -
Ohm*m
IEC 62631-3-1
Comparative tracking index
600 / -
-
IEC 60112
ASTM Data
Dielectric Strength, Short Time
20.9 / -
kV/mm
ASTM D 149
Dissipation Factor, 1 MHz
0.02 / -
-
ASTM D 150
Dielectric Constant, 1 MHz
3.7 / -
-
ASTM D 150
Volume Resistivity
1E15 / -
Ohm*cm
ASTM D 257
Other properties
dry / cond
Unit
Test Standard
Water absorption
5.7 / *
%
Sim. to ISO 62
Humidity absorption
1.8 / *
%
Sim. to ISO 62
Density
1390 / -
kg/m³
ISO 1183
Water Absorption, 24hr
0.7
%
ASTM D 570
Density
1380
kg/m³
ASTM D 792
Material specific properties
dry / cond
Unit
Test Standard
ISO Data
Viscosity number
157 / *
cm³/g
ISO 307, 1157, 1628